Polyester Extrusion TPU Material Manufacturer

Polyester Extrusion TPU Material

: http://tpu-material.com/1-3-polyester-extrusion-tpu-material/index.html

The polyester extrusion TPU material is known for its outstanding physical properties, mechanical properties and environmental performance. It is characterized by an excellent transparency, excellent processability and stable extrusion performance. This product is primarily used for thin film, easy-to-cut film, pipe, wire and cable, elastic band and shoulder straps.

Product Parameters

Product series Huafon TPU 13/23 series
Hardness: shore A80--shore D63
Operation: Extrusion
Characteristics: Excellent physical properties, mechanical properties, good transparency, excellent workability and stable extrusion performance
Main models: 1380AC, 1385AC, 1380A, 1385A, 2385A, 1388A, 1395A, 2395A, 1398A, 2398A

Technical Specifications

HF-1380AC Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1380AC	80A	13	948	85	3.6	180

HF-1385AC Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1385AC	85A	18	700	100	6	/

HF-1380A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1380A	81A	30	1000	100	4.8	150

HF-1385A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1385A	85A	32	650	110	6	120

HF-1388A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1388A	88A	30	800	130	7	/

HF-1398A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1398A	60D	30	500	180	15	/

HF-2385A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-2385A	85A	28	900	120	6	/

HF-2398A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-2398A	60D	32	500	190	15	/

Application Examples