Corrugated Conduit / Convoluted Tubing
Model: BW
Non-heat shrinkable tubing
BW convoluted tubing is non-heat shrinkable tubing manufactured from eco-friendly modified polyolefin, featuring good flame-retardancy and strong mechanical toughness while offering excellent chemical resistance to acids, alkali, salts and lubricating oil. The corrugated construction provides the non-heat shrinkable tubing with excellent bending and abrasion resistance. This convoluted tubing is primarily used to protect cabling and wire harnesses for automotive, mechanical, and many other industries requiring corrugated tubing. WOER is able to customize both convoluted non-split tubing and corrugated split tubing to meet your specific needs.
- Insulating and protecting cables and wires
- Black or orange, other colors are available as required
- Excellent thermal aging property
- Excellent cold impact strength
- Excellent behavior under reversed bending stress
- Excellent chemical resistance
- Cut-to-length and split loom tubing are also available on request
BW-PPF
Material: Polypropylene
Burning behavior according to FMVSS 302 and GB 8410-2006
RoHS and REACH compliant
Property | Test Method | Typical Performance |
Tensile strength | ASTM D2671 | 21MPa |
Elongation | ASTM D2671 | 200% |
Thermal aging (125℃×3000h) | QC/T29106 Appendix D | No cracking |
Thermal aging (150℃×240h) | QC/T29106 Appendix D | No cracking |
Cold bending test (-40℃×24h) | QC/T29106 Appendix D | No cracking |
Flexibility | QC/T29106 Appendix D | Pass |
Flame retardant property (V0) | UL94 | Pass |
Flame retardant property (combustion speed) | GB8410 -2006, FMVSS 302 | A-0mm/min |
BW-XLPEF
Material: Crosslinked Polyethylene
Burning behavior according to FMVSS 302 and GB 8410-2006
RoHS and REACH compliant
Property | Test Method | Typical Performance |
Tensile strength | ASTM D2671 | 10MPa |
Elongation | ASTM D2671 | 150% |
Thermal aging (125℃×3000h) | QC/T29106 Appendix D | No cracking |
Thermal aging (150℃×240h) | QC/T29106 Appendix D | No cracking |
Cold bending test (-55℃×24h) | QC/T29106 Appendix D | No cracking |
Flexibility | QC/T29106 Appendix D | Pass |
Flame retardant property (V0) | UL94 | Pass |
Flame retardant property (combustion speed) | GB8410 -2006, FMVSS 302 | A-0mm/min |
BW-PAF
Material: Polyamide
Burning behavior according to FMVSS 302 and GB 8410-2006
RoHS and REACH compliant
Property | Test Method | Typical Performance |
Tensile strength | ASTM D2671 | 28MPa |
Elongation | ASTM D2671 | 260% |
Thermal aging (125℃×3000h) | QC/T29106 Appendix D | No cracking |
Thermal aging (150℃×240h) | QC/T29106 Appendix D | No cracking |
Cold bending test (-40℃×24h) | QC/T29106 Appendix D | No cracking |
Flexibility | QC/T29106 Appendix D | Pass |
Flame retardant property (V0) | UL94 | Pass |
Flame retardant property (combustion speed) | GB8410-2006, FMVSS 302 | 100mm/min |
Dimensions
Inside Diameter (mm) | Outer Diameter (mm) | Min. Bending Radius (mm) | Standard Package (m) |
5.20±0.3 | 7.20±0.3 | 5 | 400/200 |
6.00±0.3 | 9.00±0.3 | 10 | 200 |
7.00±0.3 | 10.00±0.3 | 10 | 200 |
7.50±0.3 | 10.50±0.3 | 10 | 200 |
8.50±0.3 | 11.50±0.3 | 15 | 200 |
10.00±0.3 | 13.00±0.3 | 20 | 200 |
11.00±0.3 | 14.00±0.3 | 25 | 200 |
12.00±0.3 | 15.80±0.3 | 30 | 200 |
13.00±0.3 | 17.00±0.3 | 35 | 200 |
14.50±0.3 | 18.50±0.3 | 40 | 200 |
15.10±0.5 | 19.70±0.5 | 40 | 200 |
16.00±0.5 | 20.00±0.5 | 45 | 200 |
17.00±0.5 | 21.20±0.5 | 45 | 200 |
18.00±0.5 | 22.00±0.5 | 50 | 150 |
19.00±0.5 | 23.50±0.5 | 50 | 100 |
20.00±0.5 | 25.00±0.5 | 50 | 150 |
23.00±0.5 | 28.50±0.5 | 55 | 100 |
25.00±0.5 | 32.00±0.5 | 55 | 50 |
26.00±0.5 | 33.00±0.5 | 55 | 50 |
29.00±0.5 | 34.50±0.5 | 60 | 50 |
32.00±0.5 | 36.50±0.5 | 70 | 50 |
36.00±0.5 | 42.50±0.5 | 75 | 50 |