0Cr27Al7Mo2 High Resistance Alloy
Introduction:
0Cr27Al7Mo2 resistance alloy, made of FeCrAl, is featured with high resistivity, low resistance coefficient, high operating temperature and good oxidation resistance under high temperature. And the maximum applicable temperature is as high as 1400℃.
| Style | Specification | ||
| Wire | Diameter: 0.03mm-8mm | ||
| Flat strip | Width: 0.4-40mm | Thickness: 0.03-2.9mm | |
| Strip | Width: 8-250mm | Thickness: 0.1-3.0mm | |
| Foil | Width: 6-120mm | Thickness: 0.003-0.1 | |
| Rod | Diameter: 8-100mm | Length: 50-1000 mm | |
Application
When the temperature is over 1200℃, this 0Cr27Al7Mo2 resistance alloy is mainly used to make electric heating elements in single crystal furnace, fritting furnace,ceramic burn stove, heat treatment furnace and diffusion furnace.
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max | |||||||||
| 0.05 | 0.025 | 0.025 | 0.20 | Max 0.40 | 26.5~27.8 | Max 0.60 | 5.0~7.0 | Bal. | Mo 1.8-2.2 |
| Yield strength (Mpa) | Tensile strength (Mpa) | Elongation (%) | Density (g/cm3) | Resistivity (20℃) (Ω·mm2/m) | Heat conductivity (20℃) (W/(m·K)) | Average linear expansion coefficient (20℃-1000℃) (1/℃) | Specific heat capacity (20℃) (J/( kg℃)) | Melting point (℃) | Max. operating temperature (℃) | Magnetism |
| 460 | 700 | 20 | 7.10 | 1.53 | 13 | 16x10-6 | 0.49 | 1520 | 1400 | Non |
| 20℃ | 100℃ | 200℃ | 300℃ | 400℃ | 500℃ | 600℃ | 700℃ | 800℃ | 900℃ | 1000℃ | 1100℃ | 1200℃ |
| 1 | 0.997 | 0.996 | 0.994 | 0.991 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 |
Index
iron chromium aluminium alloy, resistance wire, alloy strip, NiCr alloy
Related products
Send Message
Most Recent
More
Other Products
Videos