Ceramic Grinding Media
Alumina Grinding Media
The distinctive features of the microcrystalline alumina grinding media produced by Pingxiang Hualian lie that they possess high strength, high density and low attrition loss. They are suitable for both dry and wet grinding processes. Ceramic grinding media are mainly applied for ball mills, agitators, vibro-mills and sand-mille etc. They are well received in industries of architectural ceramics, sanitary wares, enamels, zirconium silicate, kaoline, feldspar, refractories, urea-formaldehyde molding powder, paints, coating, etc.
Our company can provide two different kinds of alumina wear resistant balls formed by isostatic pressing procedure or automatic rolling procedure in accordance with customer 's requirements.
Size range of the isostatic pressed balls: Ø30mm-Ø60mm
Size range of the rolled balls: Ø1mm-Ø30mm
Technical Parameters of Alumina Grinding Media| Chemical Composition | Physical Features | Mechanical Features | ||||||
| Type | Al2O3 Wt % | SiO2 Wt % | Fe2O3 Wt % | Bulk Density g/cm3 | Attrition Loss % | Water Adsorption % | Moh's hardness | Crushing strength, Mpa |
| OD-90 | ≥ 90 | < 6 | < 0.3 | 3.3 | 0.2 | 0.1 | 8.5 | 1700 |
| OD-92 | ≥ 92 | < 5 | < 0.2 | 3.6 | 0.15 | 0.1 | 9 | 2000 |
| OD-92A | ≥ 92 | < 5 | < 0.2 | 3.65 | 0.1 | 0.1 | 9 | 2000 |
| OD-95A | ≥ 95 | < 3 | < 0.15 | 3.7 | 0.1 | 0.1 | 9.5 | 2200 |
| OD-99A | ≥ 99 | < 1 | < 0.1 | 2.0 | 0.05 | 0.1 | 9.5 | 2200 |
Note: The contents of Al2O3 and SiO2 can be decided upon customer's request.
Zirconia Grinding Media
Application
1. Electronic materials, like BaTiO3, BaCO3
2. Oil paint, printing ink, coating
3. Porcelain enamel, like zirconium silicate
4. Medicine, cosmetics
Features of Zirconia Grinding Media
1. Great grinding resistance, with an attrition loss less than four millionths.
2. High density, high grinding efficiency.
3. No contamination, without impurities.
Applicable Machines
Ø0.5-3mm grinding balls suitable for sand mill
Ø5-20mm grinding balls suitable for stirring grinder and rotary ball mill
Ø20mm grinding balls suitable for rotary ball mill
| ZrO2 content, % | ≥94.5 |
| Bulk density, kg/l | 3.6-3.8 |
| Specific gravity | 6.0 ±0.05 |
| Bending strength, Mpa | ≥900 |
| KIC MNm-3/2 | 8 |
| Crushing strength, Mpa | 7500 |
| Moh's hardness | 8.5-9 |
| Attrition loss, ppm/hr | 4 |
| Size, Ømm | 0.2-60mm |
You may also find products like:
Alumina Grinding Ball, YSZ Grinding Media, Ceramic Milling Media